New generation Fluorine monofilament studied on purpose to obtain a good elasticity, a very high knot strength and a water refraction very similar to fluorocarbon one (water = 1,34/ fluorine = 1,41 / fluorocarbon = 1,37). It is suggested the triple knot to have the maximum strength.
code | size | diameter | breaking strains |
---|---|---|---|
22501** | 50 m | 0,120 mm | 1,950/1,500 kg |
22502** | 50 m | 0,140 mm | 2,860/2,200 kg |
22503** | 50 m | 0,160 mm | 3,510/2,700 kg |
22504** | 50 m | 0,180 mm | 4,030/3,100 kg |
22505** | 50 m | 0,200 mm | 5,200/4,000 kg |
22507** | 50 m | 0,240 mm | 6,500/5,000 kg |
22508** | 50 m | 0,260 mm | 8,060/6,200 kg |
22509** | 50 m | 0,280 mm | 9,360/7,200 kg |
22510** | 50 m | 0,300 mm | 10,920/8,400 kg |
22511** | 50 m | 0,330 mm | 12,220/9,400 kg |
22512** | 50 m | 0,370 mm | 15,340/11,800 kg |
22531** | 150 m | 0,120 mm | 1,950/1,500 kg |
22532** | 150 m | 0,140 mm | 2,860/2,200 kg |
22533** | 150 m | 0,160 mm | 3,510/2,700 kg |
22534** | 150 m | 0,180 mm | 4,030/3,100 kg |
22535** | 150 m | 0,200 mm | 5,200/4,000 kg |
22537** | 150 m | 0,240 mm | 6,500/5,000 kg |
22538** | 150 m | 0,260 mm | 8,060/6,200 kg |
22539** | 150 m | 0,280 mm | 9,360/7,200 kg |
22540** | 150 m | 0,300 mm | 10,920/8,400 kg |
22541** | 150 m | 0,330 mm | 12,220/9,400 kg |
22542** | 150 m | 0,370 mm | 15,340/11,800 kg |